Posts in plating tank
Update on ONE PLATE Electroless Nickel!

Did you know companies are finding the benefits of One-Plate® are even greater as one component is easier to order, ship, and stock than three components.

Shops are finding this very convenient especially now that supply chains are strained by transport issues. 

Shops with short labor or split shifts are reporting how One-Plate® is easier to operate with less workers and lab analysis. 

And for those shops where their business level is lower due to the pandemic, they are appreciating the savings in time, energy, labor, and costs.

One-Plate® is now in 15 countries on 5 continents.

  • Plating International has increased our manufacturing capacity to meet the growing demand.

  • Single component One-Plate® EN versions are now available in low, mid, high phos and composites with Teflon, diamond, silicon carbide and boron nitride.

  • Just as the cold weather is coming, Plating International has verified the freeze resistance of the most popular One-Plate® 1001Q solution. Attached please see a photo with a typical "A" solution on the left and One-Plate® 1001Q on the right. After two weeks in a 5 degree F (-15 C) freezer, the "A" solution is frozen solid. The One-Plate® solution was just very cold. We then tested the One-Plate® solution and it plated as well as it always does, so there was no negative affect from the cold storage.

  • New technical articles and case studies are in the works..

Also, in this Covid-19 time when travel is limited, we have been having frequent video conference meetings to support plating shops and prospective customers to answer any questions they have, please don’t hesitate to reach out to set up any calls like this.

workshop.jpg
Chrome Plating : Flex Kraft Switch Mode Rectifier

Plating International Inc.’ s new video discusses why Bob the chrome plater is ready to make the switch to a Flex Kraft switch mode rectifier from his traditional SCR rectifier. Click the video below to learn more!

A Look at the Superior Poly Tank Material: Homopolymer Polypropylene vs Co-Polymer Polypropylene
download.png

Traditionally, most “polypro” tanks are made with what is called “propylene homopolymer,” or “natural polypropylene.” This type of polypropylene has a high strength-to-weight ratio and is known for its stiffness and rigidity. In the plating industry, this natural polypropylene is the go-to material for most plastic-type tanks.

There is, however, another material, called “polypropylene copolymer” which is a less common material but is nonetheless superior in many ways. This copolymer polypropylene is a type of polypropylene that has a modified polymer chain which includes a different, “random” monomer molecule (for instance, ethylene). This molecular change results in some serious changes in physical property.

Compared to homopolymer PP, copolymer PP has a much higher impact resistance, increased flexibility and durability, and a lower melting point (which results in a lower heat-sealing temperature). Copolymer PP also tends to have a better stress crack resistance and lower temperature toughness than homopolymer. At the same time they exhibit essentially the same chemical resistance, water vapor permeability, and organoleptic properties (low tatste and odour contribution).

Given the comparative advantage of copolymer PP, it seems like a no-brainer to have a copolymer PP tank over a natural polypro tank. Because the copolymer is much more flexible and less stiff than the homopolymer, it will have a longer life than a natural polypro tank, and will be more resistant to stress and impact (for example, if a heavy anode or cathode falls of the bussing to the bottom of the tank). This means they are also less likely to get damaged during delivery. Copolymer PP also has a moderately better impact strength at temperatures down to 0°C, and have limited utility down to -25°C.

Plating International offers rigid plating tanks in both propylene homopolymer and copolymer polypropylene materials. Contact us for a quote today.

Difference-Between-Copolymer-and-Homopolymer-Tabular-Form.jpg
How To Passivate Stainless Steel Plating Tanks

Properly passivated stainless steel will not plate unless contacted by a plating part or the bath is not properly maintained. They must be passivated from time to time according to the procedures established (by STI) for safety and effective passivation without contaminating the solutions or rinse tanks. Stainless steel is composed of iron (Fe); nickel (Ni); chromium (Cr) and several other minor components. Stainless steel is not resistant to chemical or physical attack. The corrosion resistance of stainless steel depends on the formation of a ‘passive surface film’ composed of nickel and chromium oxides (Cr2O3 & Ni0).

Procedure:

1. Pump bath out into the corresponding drums, tote, or tank.

2. Spray rinse the tank & plumbing, then drain any leftover bath into corresponding drums or tank.

3. Pump in 40% Nitric for Passivation from the tote into empty tank.

4. Once tank is filled with “40% Nitric for Passivation” do the following 3 things.

A. Turn on all pumps to tank.

B. Set temperature of the “40% Nitric for Passivation” to 90o F.

C. After you have completed Set 1 and 2 set timer for 3 hours.

0.jpg

5. After 3 hours are up, unplug all pumps in the tank and turn off steam,

6. Pump “40% Nitric or Passivation” into the tote.

7. Drain any leftover Nitric into a bucket through the valve behind the tank and pour back into tote.

8. Spray rinse the tank and plumbing, then drain straight to the trench.

9. Fill empty tank with city water.

10. After the tank is filled with city water do the following 3 things.

A. Turn on all pumps to tank

B. Turn on air agitation

C. Add 2000 mls of NH4OH to neutralize water (per 100 gallons of water)

11. Let mix for 10 mins.

12. Pump water back into the tote unless instructed otherwise.

13. Spray rinse the tank and plumbing, then drain straight to the trench.

14. Take out spargers and clean in tank.

15. Thoroughly spray clean tank (Walls, Plumbing, Backflush, Etc.)

16. Once tank has been thoroughly cleaned reattach spargers back onto the reactor.

17. Spray rinse the entire tank with DI water one last time.

18. The tank has now been successfully passivated & cleaned and is now ready for a bath to be pumped in or made up new after the valve is closed.

The Best of Both Worlds: Plating With Poly and Steel Tanks

One of the major decisions that plating shops have to deal with is “what kind of plating tank should I get for my plating line?” Of course, we wish the answer was as simple as the question, but the truth of the matter is it depends on a lot of different things. What are you plating? Plating chromic acid is a completely different process than zinc or cadmium plating. How much are you plating? 300 gallons or 3000 gallons? What method are you using to plate? There are so many questions to ask and factors to consider, we thought it would be nice to see it in the form of a pros/cons table:

Polypropylene_page-0001 (2).jpg

As you will see in the diagram above there are many different things to consider when choosing a plating tank. Polypropylene tanks are great for smaller bath sizes and they are well-suited for the harsh conditions provided by plating shops. Polypropylene tanks are also very durable and they are great for use with acids and alkalies, which is why you can sometimes avoid buying a liner for your tank (unless you’re plating chromic acid, which you’ll definitely still need a liner for!) Polypropylene tanks are also much more flammable than steel tanks, which can be an issue if you are using electrical heaters to heat up your bath. While steel can hold up to well over +2000°F, polypropylene melts at around 320°F. Another factor is their size limit - because of polypropylene’s lower tensile strength and modulus, you will likely need supports to prevent bulging and breaks at the seams; but steel tanks have a lot more natural support because of their higher tensile strength. However, steel tanks are vulnerable to other conditions that the polypropylene tanks will almost never encounter: they can rust and they are susceptible to pinholes, which can be very dangerous if not immediately fixed.

At the end of the day, you’re really going to have to take the time and think about what solution works best for your business needs. That’s why you should ask the experts here at Plating International. With over 40+ of working experience, we can help you well above-and-beyond all your plating needs. Contact us today for a quote on plating tanks!